低合金高強鋼中非金屬夾雜物的改性

Modification of non-metallic inclusions in high-strength low-alloy steel

  • 摘要: 借助熱力學軟件Thermo-Calc和ASPEX自動掃描電鏡等分析手段,研究了低合金高強鋼精煉過程渣-鋼反應和鈣處理對夾雜物改性行為的影響.通過提高爐渣堿度和w(CaO)/w(Al2O3)值以及降低爐渣氧化性等措施,鈣處理前鋼中Al2O3夾雜物轉變為靠近1600℃液相區的CaO-MgO-Al2O3復合夾雜物和少量的MgO·Al2O3尖晶石.在渣-鋼反應對Al2O3部分變性的基礎上,鈣線喂入量每爐由優化前的800 m減少到300 m仍能達到夾雜物改性的目的.

     

    Abstract: The influences of slag-metal reaction and calcium treatment on inclusion modification in high-strength low-alloy steel were studied by means of Thermo-Calc thermodynamic software and ASPEX automated scanning electron microscope. The results of industrial trials show that by increasing the basicity, reducibility and w(CaO)/w(Al2O3) of slag, Al2O3 inclusions are partially modified to CaO-MgO-Al2O3 complex inclusions nearby the liquid phase zone at 1 600℃, as well as a few MgO·Al2O3 spinel. On the basis of this change, the purpose of inclusion modification is still achieved with the addition of CaSi-wire decreasing from 800 m to 300 m for a heat.

     

/

返回文章
返回
<span id="fpn9h"><noframes id="fpn9h"><span id="fpn9h"></span>
<span id="fpn9h"><noframes id="fpn9h">
<th id="fpn9h"></th>
<strike id="fpn9h"><noframes id="fpn9h"><strike id="fpn9h"></strike>
<th id="fpn9h"><noframes id="fpn9h">
<span id="fpn9h"><video id="fpn9h"></video></span>
<ruby id="fpn9h"></ruby>
<strike id="fpn9h"><noframes id="fpn9h"><span id="fpn9h"></span>
www.77susu.com