摘要: 典型鐵合金渣（硅錳渣，鎳鐵渣，鉻鐵渣）面臨產量大、利用率低等緊迫問題。目前，我國對鐵合金渣的利用主要集中于水泥、混凝土等傳統建筑材料，但是其能耗大和產品價值相對局限。隨著市場需求以及環保能源意識的提高，對鐵合金渣的綜合利用不斷從傳統建筑材料向具有低能耗、高附價值的新型材料方向轉型。本文簡要介紹了這三種典型鐵合金渣的來源及其分類情況，系統分析了它們的化學成分及其礦物組成的差異性，重點概述了它們在水泥、混凝土等傳統建筑材料，以及在地質聚合物、無機礦物纖維、微晶玻璃、人造輕骨料、耐火材料、新型墻體材料、特色功能陶瓷等新型材料領域應用的國內外最新研究進展，分類總結不同種類鐵合金渣應用于不同材料的優缺點，并對其今后的利用方向與途徑提出了展望，指出了要進一步研究并突破主要利用方式的限制瓶頸、制定并完善相關應用及污染控制標準、以及深入開發并推廣高附加值產品的重點發展方向。Abstract: Three typical ferroalloy slags, namely, silicon–manganese, nickel–iron, and chrome–iron slags, are produced in large quantities as by-products. This is because they are not efficiently utilized, which creates lots of pressure on environmental capacity and development of enterprises. At present, comprehensive utilization of ferroalloy slags is mainly concentrated on the traditional building materials such as cement and concrete. Although the construction industry consumes a large amount of ferroalloy slags, their high-energy consumption and relatively limited product value limit their maximum utilization. With the increasing market demand and improvement of energy and environmental awareness, the research on rational utilization of ferroalloy slags has been changing from its use as raw materials in traditional building materials to use as raw materials to produce new products with comparatively lower energy consumption and higher product value, which explores the possibility of slag reutilization in other fields. Based on the quality requirements of different ferroalloys, there are significant differences in the requirements of the raw materials and different smelting processes. As a result, different types of ferroalloy slags, having different physical and chemical properties, are produced. This study briefly presented the uses of the silicon–manganese, nickel–iron, and chrome–iron slags. It also showed how to classify these three typical ferroalloy slags. The differences of their chemical and mineral phase composition were also systematically analyzed in this study, which discussed different properties of different slags and provided the basic theoretical guidelines on how to efficiently utilize these slags. This study also emphatically summarized the latest domestic and foreign research advancements about their utilization in traditional building materials such as cement and concrete, and in new functional materials such as geopolymer, inorganic mineral fiber, microcrystalline glass, artificial light aggregate, and refractory materials required to build walls and as alternative raw materials to prepare functional ceramics. Based on the results of this study, we summarized the advantages and disadvantages of using the abovementioned ferroalloy slags as raw materials to generate different materials, and put forward the prospects for its future utilization direction and approach. The study also guided the key development areas for further studying and breaking through the bottleneck of the main utilization mode, formulating and improving the relevant application and pollution control standards, and developing and promoting high value-added products.
-
圖 4 鎳渣耐火材料的耐火性能及物相轉變隨鎂砂添加量的變化示意圖[63]
Figure 4. Effect of magnesia addition on the refractoriness and phase of nickel slag refractory material
表 1 典型鐵合金渣的主要化學成分及礦物組成
Table 1. Chemical and mineral compositions of some ferroalloy slags
Type Main chemical composition/% Main mineral composition Reference CaO SiO2 Al2O3 MgO Fe2O3 MnO Cr2O3 Silicon?manganese slag 20.0 32.3 16.1 4.55 0.3 20.4 ― Bustamite (CaMnSi2O6)Anorthite (CaAl2Si2O8)Cristobalite (SiO2) Choi et al.[3] Blast furnace nickel?iron slag 24.99 26.19 34.70 6.00 1.78 1.73 1.59 Dicalcium silicate(2CaO·SiO2)Magnesium aluminum spinel (MgAl2O4) Yin et al.[4] Electric furnacenickel?iron slag 0.29 58.10 2.29 26.50 11.0 ― ― Enstatite (Mg2Si2O6)Forsterite (MgSiO4) Choi et al.[5] High carbonchrome?iron slag 2.06 29.61 22.79 37.88 1.69 ― 2.06 Forsterite (MgSiO4)Magnesium chrome spinel (Mg(Al1.5Cr0.5)O4)Magnesium aluminum
spinel (MgAl2O4)Bai et al.[6] Medium & low carbonchrome-iron slag 47.35 30.77 9.03 6.9 1.3 ― 4.15 Dicalcium silicate (2CaO·SiO2)Manganolite (3CaO·MgO·2SiO2)Gehlenite (2CaO·Al2O3·SiO2) Hao[7] 
下載: 導出CSV
表 2 典型鐵合金渣用于水泥混合材的部分研究成果
Table 2. Some results of the research on the uses of some ferroalloy slags as raw materials used in cement admixture
Types Research results Reference Silicon?manganese slag The authors found that the cement products with 15% slag in mass showed good chemical resistance. After 56-d of exposure to the corrosion solution, the weight of the cement products was basically the same. Besides, the addition of silicon manganese slag reduced the void structure, which is conducive to resisting the external extreme environment. Frías et al.[15] Silicon?manganese slag The authors prepared low-calorie composite cement using silico-manganese slag, fly ash and medical waste, which achieved a 28-d compressive strength of 34 MPa and a stability value of 8.95, meeting the requirements of the construction industry. Singh et al.[16] High?magnesium nickel?iron slag The authors prepared the cement slurry mixed with high magnesium nickel?iron slag, and found that the water demand and setting time did not change significantly when it was used to replace 50% cement. Under the accelerated curing at 80 ℃ for 120 d, although the magnesium content was high, the product did not expand because the magnesium existed in the form of stable Mg olivine ferrite and did not participate in the hydration reaction. Rahman et al.[17] Blast furnace nickel?iron slag The authors prepared the cement with 20% blast furnace nickel?iron slag. Compared with pure cement products, it required less water and had a longer setting time. The addition of nickel iron slag would reduce the hydration rate in the early stage, and increased the strength of its products in the later stage, achieving a 28-d compressive strength greater than 45 MPa. Katsiotis et al.[18]
下載: 導出CSV
表 3 典型鐵合金渣用于混凝土的部分研究成果
Table 3. Some results of research on some ferroalloy slags used in concrete
Types Function Research Results Reference Silicon?manganese slag Admixture The authors mixed silicon manganese slag, limestone and cement grinding aids to produce composite micropowder, and found that the fluidity of the concrete prepared by replacing the cement with 30% fine powder was comparable to that of the whole cement, besides its compressive strength was far higher than that of the concrete prepared with 30% pure silicon-manganese slag. Lv et al.[32] Nickel?iron slag Admixture The author replaced part of the cement with electric furnace nickel?iron slag to prepare concrete materials with excellent performance, whose strength could meet that of full cement concrete. Besides, the composition of raw materials was reduced by 15 US dollars, and the CO2 emission was reduced by 4%?24%. Kim et al.[33] Nickel?iron slag Fine aggregate In this paper, the durability of ferronickel slag as concrete fine aggregate was studied. The results showed that when 27% nickel?iron slag replaced sand, the corrosion resistance of concrete to sulfate increased, but it had no significant effect on chloride ion corrosion. Liu et al.[34] High?carbonchrome?
iron slagFine aggregate The concrete products was prepared by cement and partial granular high?carbon chrome?iron slag which was used as fine aggregate instead of a part of natural river sand. When the amount of slag was 10%, the strength indicators of concrete products were equivalent to those of pure natural sand-based concrete. Toxic leaching experiments showed that the leaching concentration of chromium was far less than the standard concentration threshold. Dash et al.[35]
下載: 導出CSV
表 4 典型鐵合金渣用于多種產品的優勢及問題
Table 4. Advantages and problems of products prepared by some ferroalloy slags
Product Slag Advantage Problem Standard Industrialization feasibility Cememnt Admixture Silicon-manganese slag; Blast furnace Nickel-iron slag; Medium & low-carbon chrome-iron slag Large dosage (40%?60%); high activity; low water demand and small hydration heat; small volume expansion and small possibility of powdering; mature technology The reaction in the early stage of hydration is slow and the intensity is low. In the later stage of hydration, the reaction is fast and the intensity is high. The setting time is longer. YB/T 4229―2010 Simple Raw meal Electric furnace nickel-iron slag; High-carbon chrome-iron slag Relatively large dosage (15%?30%); reducing the amount of free CaO in clinker Cement products have low activity and require the use of large amounts of adjuvants. The market acceptance is low. Concrete Admixture Silicon-manganese slag; Blast furnace nickel-iron slag; Medium & low-carbon chrome-iron slag Large amount (30%?60%); reducing water consumption and improving fluidity; improving the density of aggregate-slurry transition area; strong operability The MgO content is high, and the long-term stability of the concrete is potentially dangerous. The particle size of the raw material is small, and the possibility of heavy metal elements leaching is high. YB/T 4229-2010JIS A5011-2―2003 Simple Aggregate Electric furnace nickel-iron slag; High-carbon chrome-iron slag High hardness and good abrasion resistance; no need for ultra-fine processing and high operability; making up for the shortage of raw materials such as river sand If the content of glass phase is high, the expansion of concrete may be caused by the strong alkali silica reaction. Geopolymer Silicon-manganese slag; Blast furnace nickel-iron slag; Medium & low-carbon chrome-iron slag No high temperature sintering and hydration reactions are required, and the preparation method is simple. There is no transition area of ordinary cement concrete. The three-dimensional network structure gel makes the corrosion resistance stronger. The gel needs to be thermally cured at high pH values, which is not difficult in actual operation.It is necessary to develop simple and efficient solid activators to replace highly alkaline solutions; No Simple Inorganic mineral fiber Silicon-manganese slag; Blast/electric furnace nickel-iron slag; Medium & low/high carbon chrome-iron slag The combination of product preparation and slag sensible heat recovery has the advantages of low cost and low energy consumption; It is widely used and has high added value. Due to the difference in composition and temperature, the slag viscosity and acidity match fluctuate greatly. The high MgO and Al2O3 of high carbon ferrochrome slag and electric furnace nickel iron slag make the viscosity difficult to control. No Moderate Glass ceramic Silicon-manganese slag; Blast/electric furnace nickel-iron slag; Medium & low/high carbon chrome-iron slag High fluctuation range of raw material composition;use with a variety of ferroalloy slag; high degree of solid waste utilization (50%?80%); high market acceptance It is prepared by high-temperature melting method with high energy consumption, and the energy consumption is high. The procedure is relatively complicated and the preparation time is long. It will take a long time to observe whether the stability problems of powdered glass and other glass ceramics have been used for a long time. No Moderate Artificial light aggregate Silicon-manganese slag; Electric furnace nickel-iron slag; High-carbon chrome-iron slag The porous structure increases the density of the aggregate slurry. The water absorption is small, which is conducive to later stability. Large amount of solid waste doping (60%?80%). The requirements for raw material composition and firing system are relatively strict to ensure the best balance of pores and liquid phase. The strength is relatively limited, and it is relatively lagging behind for structural engineering research. No Simple Refractory material Electric furnace nickel-iron slag; High-carbon chrome-iron slag Easier formation of forsterite phase and spinel phase because of the high content of magnesium and aluminum; variety of products; high degree of solid waste utilization and large added value of products Affected by products and processes, the magnesium and aluminum content fluctuates greatly, which causes trouble for actual operation.After being corroded by gas and liquid for a long time, heavy metals are easily dissolved out and cause pollution. No Moderate New wall materials (autoclaved brick, autoclaved aerated concrete) Silicon-manganese slag; Blast/electric furnace nickel-iron slag;Medium & low/high carbon chrome-iron slag The preparation method is relatively simple, low cost, and low energy consumption.The utilization degree of solid waste is high and the added value of products is large.The technical guidance of high efficiency, high sound insulation, and high thermal resistance is conducive to the promotion and use of energy-saving non-bearing wall materials. The general cementitious material has a long gelation time, which is not conducive to rapid demoulding treatment. The study of fast high-strength gelling materials is the key.Because of the contradiction between light weight and high strength, mineral fiber can be added to increase the performance. GB/T 32989―
2016Simple Featured functional materials (structural ceramics, porous ceramics, porous polymer particles) Electric furnace nickel-iron slag; High-carbon chrome-iron slag (structuralceramics); Silicon-manganese slag; High-carbon chrome-iron slag (porous ceramics) The incorporation of slag will reduce the sintering temperature without affecting its performance. The utilization degree of solid wastes and the added value of products are relatively higher. Porous polymer particles are used in sound-absorbing materials, which are not easy to pulverize and settle, and the preparation method is simple and operable. For spinel corundum structural ceramics, the requirements for raw materials are relatively strict, and the preparation process is relatively complex, and the preparation time is long.The development of slag-based sound-absorbing materials is not yet perfect, and lacks in-depth theoretical and technical support. No Difficult
下載: 導出CSV
www.77susu.com<span id="fpn9h"><noframes id="fpn9h"><span id="fpn9h"></span> <span id="fpn9h"><noframes id="fpn9h"> <th id="fpn9h"></th> <strike id="fpn9h"><noframes id="fpn9h"><strike id="fpn9h"></strike> <th id="fpn9h"><noframes id="fpn9h"> <span id="fpn9h"><video id="fpn9h"></video></span> <ruby id="fpn9h"></ruby> <strike id="fpn9h"><noframes id="fpn9h"><span id="fpn9h"></span> -
參考文獻
[1] Zhang Y Z, Li Y, Cang D Q. Present research and tendency of comprehensive utilization of the ferroalloy-slag. Energy Metall Ind, 2013, 32(5): 44 doi: 10.3969/j.issn.1001-1617.2013.05.012張亞洲, 李宇, 蒼大強. 鐵合金渣綜合利用的研究現狀及發展趨勢. 冶金能源, 2013, 32(5):44 doi: 10.3969/j.issn.1001-1617.2013.05.012 [2] Song Y X, Lan S D, Di J H, et al. Present situation and development trend of comprehensive utilization of ferroalloy slag in China. China Metall, 2017, 27(4): 73宋耀欣, 蘭思東, 邸久海, 等. 中國鐵合金爐渣綜合利用現狀與發展趨勢. 中國冶金, 2017, 27(4):73 [3] Choi S, Kim J, Oh S, et al. Hydro-thermal reaction according to the CaO/SiO2 mole-ratio in silico-manganese slag. J Mater Cycles Waste Manage, 2017, 19(1): 374 doi: 10.1007/s10163-015-0431-6 [4] Yin S H, Ma J, Yan B, et al. Characteristics of several different nickel slags and their feasibility for use in cement and concrete. Bull Chin Ceram Soc, 2019, 38(7): 2268殷素紅, 馬健, 顏波, 等. 幾種不同鎳渣的特性及其用于水泥和混凝土中的可行性. 硅酸鹽通報, 2019, 38(7):2268 [5] Choi Y C, Choi S. Alkali-silica reactivity of cementitious materials using ferro-nickel slag fine aggregates produced in different cooling conditions. Constr Build Mater, 2015, 99: 279 doi: 10.1016/j.conbuildmat.2015.09.039 [6] Bai Z T, Qiu G B, Peng B, et al. Synthesis and characterization of glass-ceramics prepared from high-carbon ferrochromium slag. RSC Adv, 2016, 6(58): 52715 doi: 10.1039/C6RA06245H [7] Hao X T. Preparation of Low Temperature Ceramic Cementitious Materials by Activation of Ferrochrome Slag [Dissertation]. Kunming: Kunming University of Science and Technology, 2016郝旭濤. 鉻鐵渣活化制備低溫陶瓷膠凝材料[學位論文]. 昆明: 昆明理工大學, 2016 [8] Lu H F, Tian W G, Xu J L, et al. Research progress on comprehensive utilization of ferronickel slag. Mater Rev, 2018, 32(Suppl 2): 435陸海飛, 田偉光, 徐佳林, 等. 紅土鎳礦冶煉鎳鐵廢渣綜合利用的研究進展. 材料導報, 2018, 32(增刊2): 435 [9] Li K Q, Feng L, Gao S J. Preparation of cementitious materials for backfilling by using nickel slag. Chin J Eng, 2015, 37(1): 1李克慶, 馮琳, 高術杰. 鎳渣基礦井充填用膠凝材料的制備. 工程科學學報, 2015, 37(1):1 [10] Zhang X F, Ni W, Wu J Y, et al. Hydration mechanism of a cementitious material prepared with Si?Mn slag. Int J Miner Metall Mater, 2011, 18(2): 234 doi: 10.1007/s12613-011-0428-7 [11] Nath S K, Kumar S. Evaluation of the suitability of ground granulated silico-manganese slag in Portland slag cement. Constr Build Mater, 2016, 125: 127 doi: 10.1016/j.conbuildmat.2016.08.025 [12] Wu Q S, Wu Y, Tong W H, et al. Utilization of nickel slag as raw material in the production of Portland cement for road construction. Constr Build Mater, 2018, 193: 426 doi: 10.1016/j.conbuildmat.2018.10.109 [13] Hao X T, Zhou X T, Cai F W, et al. Property of ferrochrome slag based low-temperature cementitious material. Bull Chin Ceram Soc, 2015, 34(7): 2013郝旭濤, 周新濤, 蔡發萬, 等. 鉻鐵渣基低溫陶瓷膠凝材料的性能研究. 硅酸鹽通報, 2015, 34(7):2013 [14] Hao X T, Zhou X T, Luo Z Q, et al. Effects of compound admixtures on the properties of ferrochrome slag based composite materials. J Funct Mater, 2015, 46(13): 13029 doi: 10.3969/j.issn.1001-9731.2015.13.006郝旭濤, 周新濤, 羅中秋, 等. 復合型外加劑對鉻鐵渣基復合材料性能的影響. 功能材料, 2015, 46(13):13029 doi: 10.3969/j.issn.1001-9731.2015.13.006 [15] Frías M, de Rojas M I S, Rodríguez C. The influence of SiMn slag on chemical resistance of blended cement pastes. Constr Build Mater, 2009, 23(3): 1472 doi: 10.1016/j.conbuildmat.2008.06.012 [16] Singh G V P B, Subramaniam K V L. Production and characterization of low-energy Portland composite cement from post-industrial waste. J Clean Prod, 2019, 239: 118024 doi: 10.1016/j.jclepro.2019.118024 [17] Rahman M A, Sarker P K, Shaikh F U A, et al. Soundness and compressive strength of Portland cement blended with ground granulated ferronickel slag. Constr Build Mater, 2017, 140: 194 doi: 10.1016/j.conbuildmat.2017.02.023 [18] Katsiotis N S, Tsakiridis P E, Velissariou D, et al. Utilization of ferronickel slag as additive in Portland cement: a hydration leaching study. Waste Biomass Valor, 2015, 6(2): 177 doi: 10.1007/s12649-015-9346-7 [19] Alahrache S, Winnefeld F, Champenois J B, et al. Chemical activation of hybrid binders based on siliceous fly ash and Portland cement. Cem Concr Compos, 2016, 66: 10 doi: 10.1016/j.cemconcomp.2015.11.003 [20] Haha M B, Le Saout G, Winnefeld F, et al. Influence of activator type on hydration kinetics, hydrate assemblage and microstructural development of alkali activated blast-furnace slags. Cem Concr Res, 2011, 41(3): 301 doi: 10.1016/j.cemconres.2010.11.016 [21] Piyapanuwat R, Asavapisit S. Performance of lime-BHA solidified plating sludge in the presence of Na2SiO3 and Na2CO3. J Environ Manage, 2011, 92(9): 2222 doi: 10.1016/j.jenvman.2011.04.004 [22] Allahverdi A, Ahmadnezhad S. Mechanical activation of silicomanganese slag and its influence on the properties of Portland slag cement. Powder Technol, 2014, 251: 41 doi: 10.1016/j.powtec.2013.10.023 [23] Kumar S, García-Tri?anes P, Teixeira-Pinto A, et al. Development of alkali activated cement from mechanically activated silico-manganese (SiMn) slag. Cem Concr Compos, 2013, 40: 7 doi: 10.1016/j.cemconcomp.2013.03.026 [24] Liu L Y, Liu Y, Zhang K, et al. Study on chemical activation of nickel iron slag-cement composite cementitious material. Cem Eng, 2016(2): 8劉梁友, 劉云, 張康, 等. 鎳鐵渣-水泥復合膠凝材料化學活化的研究. 水泥工程, 2016(2):8 [25] Zhou X T, Hao X T, Ma Q M, et al. Effects of compound chemical activators on the hydration of low-carbon ferrochrome slag-based composite cement. J Environ Manage, 2017, 191: 58 doi: 10.1016/j.jenvman.2016.12.048 [26] Navarro R, Alcocel E G, Sánchez I, et al. Mechanical properties of alkali activated ground SiMn slag mortars with different types of aggregates. Constr Build Mater, 2018, 186: 79 doi: 10.1016/j.conbuildmat.2018.07.093 [27] Qi A, Liu X H, Wang Z W, et al. Mechanical properties of the concrete containing ferronickel slag and blast furnace slag powder. Constr Build Mater, 2020, 231: 117120 doi: 10.1016/j.conbuildmat.2019.117120 [28] Acharya P K, Patro S K. Acid resistance, sulphate resistance and strength properties of concrete containing ferrochrome ash (FA) and lime. Constr Build Mater, 2016, 120: 241 doi: 10.1016/j.conbuildmat.2016.05.099 [29] Jena S, Panigrahi R. Performance assessment of geopolymer concrete with partial replacement of ferrochrome slag as coarse aggregate. Constr Build Mater, 2019, 220: 525 doi: 10.1016/j.conbuildmat.2019.06.045 [30] Saha A K, Sarker P K. Sustainable use of ferronickel slag fine aggregate and fly ash in structural concrete: mechanical properties and leaching study. J Clean Prod, 2017, 162: 438 doi: 10.1016/j.jclepro.2017.06.035 [31] Shareef U, Cheela V R S, Raju S G. Study on physical and mechanical properties of quartzite and silico-manganese slag as alternative material for coarse aggregate. Int J Sci Res Dev, 2015, 3(09): 72 [32] Lv X X, Tian X K, Yang C, et al. Manganese residues waste on the application of sulfur concrete production. China Manganese Ind, 2010, 28(2): 47 doi: 10.3969/j.issn.1002-4336.2010.02.013呂曉昕, 田熙科, 楊超, 等. 錳渣廢棄物在硫磺混凝土生產中的應用. 中國錳業, 2010, 28(2):47 doi: 10.3969/j.issn.1002-4336.2010.02.013 [33] Kim H, Lee C H, Ann K Y. Feasibility of ferronickel slag powder for cementitious binder in concrete mix. Constr Build Mater, 2019, 207: 693 doi: 10.1016/j.conbuildmat.2019.02.166 [34] Liu X M, Li T Y, Tian W G, et al. Study on the durability of concrete with FNS fine aggregate. J Hazard Mater, 2020, 381: 120936 doi: 10.1016/j.jhazmat.2019.120936 [35] Dash M K, Patro S K. Performance assessment of ferrochrome slag as partial replacement of fine aggregate in concrete. Eur J Environ Civil Eng, 2018: 1 [36] Karakoc M B, Türkmen ?, Mara? M M, et al. Sulfate resistance of ferrochrome slag based geopolymer concrete. Ceram Int, 2016, 42(1): 1254 doi: 10.1016/j.ceramint.2015.09.058 [37] Teing T T, Huat B B K, Shukla S K, et al. Effects of alkali-activated waste binder in soil stabilization. Int J GEOMATE, 2019, 17(59): 82 [38] Liao X W, Chen J, Fan T F, et al. Soil of heavy metal composite pollution by geological polymer stabilization. Chin J Environ Eng, 2018, 12(7): 2056 doi: 10.12030/j.cjee.201712077廖希雯, 陳杰, 范天鳳, 等. 地質聚合物固化穩定化重金屬復合污染土壤. 環境工程學報, 2018, 12(7):2056 doi: 10.12030/j.cjee.201712077 [39] Yan C J, Guo L, Ren D M, et al. Novel composites based on geopolymer for removal of Pb (II). Mater Lett, 2019, 239: 192 doi: 10.1016/j.matlet.2018.12.105 [40] Li Q Y, He Y, Xu M X, et al. Study on the removal of Ca2+ and Mg2+ in water by the geopolymer-based inorganic membrane. J Funct Mater, 2017, 48(1): 1215李巧云, 賀艷, 徐夢雪, 等. 地質聚合物基無機膜去除水中鈣、鎂離子的研究. 功能材料, 2017, 48(1):1215 [41] Li K, Lu D Y, Li M H, et al. Research progress of porous geopolymers for thermal insulation. Mater Rev, 2015, 29(23): 58李款, 盧都友, 李孟浩, 等. 多孔地質聚合物保溫材料研究進展. 材料導報, 2015, 29(23):58 [42] Davidovits J. Geopolymers: inorganic polymeric new materials. J Therm Anal, 1991, 37(8): 1633 doi: 10.1007/BF01912193 [43] Nath S K, Kumar S. Influence of granulated silico-manganese slag on compressive strength and microstructure of ambient cured alkali-activated fly ash binder. Waste Biomass Valor, 2019, 10(7): 2045 doi: 10.1007/s12649-018-0213-1 [44] Nath S K. Geopolymerization behavior of ferrochrome slag and fly ash blends. Constr Build Mater, 2018, 181: 487 doi: 10.1016/j.conbuildmat.2018.06.070 [45] Karako? M B, Türkmen ?, Mara? M M, et al. Mechanical properties and setting time of ferrochrome slag based geopolymer paste and mortar. Constr Build Mater, 2014, 72: 283 doi: 10.1016/j.conbuildmat.2014.09.021 [46] Komnitsas K, Zaharaki D, Bartzas G. Effect of sulphate and nitrate anions on heavy metal immobilisation in ferronickel slag geopolymers. Appl Clay Sci, 2013, 73: 103 doi: 10.1016/j.clay.2012.09.018 [47] Yu Q Q, Li S L, Li H, et al. Synthesis and characterization of Mn-slag based geopolymer for immobilization of Co. J Clean Prod, 2019, 234: 97 doi: 10.1016/j.jclepro.2019.06.149 [48] He P Y, Zhang Y J, Chen H, et al. Development of an eco-efficient CaMoO4/electroconductive geopolymer composite for recycling silicomanganese slag and degradation of dye wastewater. J Clean Prod, 2019, 208: 1476 doi: 10.1016/j.jclepro.2018.10.176 [49] Kim Y, Kim M, Sohn J, et al. Applicability of gold tailings, waste limestone, red mud, and ferronickel slag for producing glass fibers. J Clean Prod, 2018, 203: 957 doi: 10.1016/j.jclepro.2018.08.230 [50] Yin X. The research on preparation of inorganic fiber by using high temperature ferronickel molten slag. Non-Ferrous Min Metall, 2013, 29(5): 48 doi: 10.3969/j.issn.1007-967X.2013.05.015尹雪. 利用鎳鐵冶煉高溫爐渣制備超細礦物無機纖維的研究. 有色礦冶, 2013, 29(5):48 doi: 10.3969/j.issn.1007-967X.2013.05.015 [51] Liu J, Nie Q Q, Han Y X, et al. Modified mechanism of asphalt by nickel-ferrous slag fiber. J Northeast Univ Nat Sci, 2018, 39(6): 862劉杰, 聶巧巧, 韓躍新, 等. 鎳鐵礦渣纖維對道路瀝青的改性機理. 東北大學學報: 自然科學版, 2018, 39(6):862 [52] Tang Y Y. The Test and Design of Heat Silicon Managanese Ore Furnace Slag Produce Mineral Wool [Dissertation]. Xi'an: Xi'an University of Architecture and Technology, 2015唐洋洋. 硅錳礦熱爐渣生產礦渣棉的試驗和設計[學位論文]. 西安: 西安建筑科技大學, 2015 [53] Zhao G Z, Zhang L L, Cang D Q. Pilot trial of detoxification of chromium slag in cyclone furnace and production of slag wool fibres. J Hazard Mater, 2018, 358: 122 doi: 10.1016/j.jhazmat.2018.06.061 [54] Bai Z T, Qiu G B, Yue C S, et al. Crystallization kinetics of glass-ceramics prepared from high-carbon ferrochromium slag. Ceram Int, 2016, 42(16): 19329 doi: 10.1016/j.ceramint.2016.09.102 [55] Ljatifi E, Kamusheva A, Grozdanov A, et al. Optimal thermal cycle for production of glass-ceramic based on wastes from ferronickel manufacture. Ceram Int, 2015, 41(9): 11379 doi: 10.1016/j.ceramint.2015.05.098 [56] Zhou K J, Zhao Q L, Zhang Y L. Crystallization properties of the glass ceramics prepared from iron-rich nickel slag. Universal J Mater Sci, 2017, 5(2): 52 doi: 10.13189/ujms.2017.050203 [57] Chen K, Ke C M, Zhang J H. Crystallization properties of silicomanganese slag-based CaO?MgO?Al2O3?SiO2 system glass-ceramics. J Wuhan Univ Sci Technol, 2015, 38(5): 346陳坤, 柯昌明, 張錦化. 硅錳渣基CaO?MgO?Al2O3?SiO2系礦渣微晶玻璃晶化性能研究. 武漢科技大學學報, 2015, 38(5):346 [58] Li Y, Yi Y D, Chen K Y, et al. Optimization of performance and composition for glass ceramics prepared from mixing molten slags. Chin J Eng, 2019, 41(10): 1288李宇, 伊耀東, 陳奎元, 等. 冶金熔渣混合制備微晶玻璃的組成及性能優化. 工程科學學報, 2019, 41(10):1288 [59] Wang Z J, Ni W, Li K Q, et al. Crystallization characteristics of iron-rich glass ceramics prepared from nickel slag and blast furnace slag. Int J Miner Metall Mater, 2011, 18(4): 455 doi: 10.1007/s12613-011-0462-5 [60] Zhang S H, Liu L B, Tan K F, et al. Influence of burning temperature and cooling methods on strength of high carbon ferrochrome slag lightweight aggregate. Constr Build Mater, 2015, 93: 1180 doi: 10.1016/j.conbuildmat.2015.04.045 [61] Liu H, Liao Q L, Liu L B, et al. Effects of calcination system on properties of lightweight aggregate produced from high carbon ferrochrome slag. Non-Metallic Mines, 2015, 38(6): 37 doi: 10.3969/j.issn.1000-8098.2015.06.011劉輝, 廖其龍, 劉來寶, 等. 燒成制度對高碳鉻鐵合金渣多孔骨料性能的影響. 非金屬礦, 2015, 38(6):37 doi: 10.3969/j.issn.1000-8098.2015.06.011 [62] Sahu N, Biswas A, Kapure G U. Development of refractory material from water quenched granulated ferrochromium slag. Miner Process Extract Metall Rev, 2016, 37(4): 255 doi: 10.1080/08827508.2016.1181630 [63] Gu F Q, Peng Z W, Zhang Y B, et al. Facile route for preparing refractory materials from ferronickel slag with addition of magnesia. ACS Sustainable Chem Eng, 2018, 6(4): 4880 doi: 10.1021/acssuschemeng.7b04336 [64] Tang H M, Peng Z W, Gu F Q, et al. Alumina-enhanced valorization of ferronickel slag into refractory materials under microwave irradiation. Ceram Int, 2020, 46(5): 6828 doi: 10.1016/j.ceramint.2019.11.176 [65] Li Q, Qian F F, Fu Q X, et al. Research of lightweight forsterite-spinel refractory from nickel slag and rice hull. Non-Metallic Mines, 2019, 42(4): 41 doi: 10.3969/j.issn.1000-8098.2019.04.012李琦, 錢烽烽, 付啟新, 等. 鎳渣/稻殼研制輕質鎂橄欖石-尖晶石耐火材料. 非金屬礦, 2019, 42(4):41 doi: 10.3969/j.issn.1000-8098.2019.04.012 [66] Wu Q S, Guang J M, Li S P, et al. Development of autoclaved aerated concrete from mechanically activated magnesium-rich nickel slag. J Mater Civil Eng, 2018, 30(7): 04018134 doi: 10.1061/(ASCE)MT.1943-5533.0002330 [67] Lou G H, Cao D S, Jiang W G, et al. Research of autoclaved brick technology prepared by ferronickel slag. Bull Chin Ceram Soc, 2018, 37(5): 1799婁廣輝, 曹德生, 姜衛國, 等. 鎳鐵渣制備蒸壓磚工藝技術研究. 硅酸鹽通報, 2018, 37(5):1799 [68] Gencel O, Sutcu M, Erdogmus E, et al. Properties of bricks with waste ferrochromium slag and zeolite. J Clean Prod, 2013, 59: 111 doi: 10.1016/j.jclepro.2013.06.055 [69] Yildiz ?, Gül R. An investigation of utilization of ferrochrome slag in brick production. Int J Innov Res Rev, 2017, 2(1): 11 [70] Feng Z Z, Wu Q S, Zhang C S, et al. Preparation and properties of nickel slag based foam glass. Bull Chin Ceram Soc, 2017, 36(5): 1740馮楨哲, 吳其勝, 張長森, 等. 鎳渣基泡沫玻璃的制備及其性能研究. 硅酸鹽通報, 2017, 36(5):1740 [71] Ren Y H, Ren Q, Wu X L, et al. Recycling of solid wastes ferrochromium slag for preparation of eco-friendly high-strength spinel–corundum ceramics. Mater Chem Phys, 2020, 239: 122060 doi: 10.1016/j.matchemphys.2019.122060 [72] Liu C B, Liu L B, Tan K F, et al. Fabrication and characterization of porous cordierite ceramics prepared from ferrochromium slag. Ceram Int, 2016, 42(1): 734 doi: 10.1016/j.ceramint.2015.08.174 [73] Li Y T, Zheng S J, Mao Z G, et al. Study and application of sound absorption properties of porous materials with polymerized particles prepared by waste Ni?Fe slag. Noise Vib Control, 2018, 38(3): 172 doi: 10.3969/j.issn.1006-1355.2018.03.033李云濤, 鄭雙金, 毛志剛, 等. 鎳鐵渣多孔聚合微粒吸聲材料研究及應用. 噪聲與振動控制, 2018, 38(3):172 doi: 10.3969/j.issn.1006-1355.2018.03.033 [74] Wang G R, Zhang J, Liu L, et al. Novel multi-metal containing MnCr catalyst made from manganese slag and chromium wastewater for effective selective catalytic reduction of nitric oxide at low temperature. J Clean Prod, 2018, 183: 917 doi: 10.1016/j.jclepro.2018.02.207 [75] Wang G R, Zhang J, Zhou J Z, et al. Production of an effective catalyst with increased oxygen vacancies from manganese slag for selective catalytic reduction of nitric oxide. J Environ Manage, 2019, 239: 90 doi: 10.1016/j.jenvman.2019.03.056 [76] Kryukov R E, Kozyrev N A, Prokhorenko O D, et al. Quality of weld seams produced with flux based on silicomanganese slag. Steel Transl, 2017, 47(7): 440 doi: 10.3103/S0967091217070051 [77] Zhang X L, Guo S L, Chen L, et al. Characterization and Ca2+ exchange capacity of zeolites synthesized by manganese slag. Bull Chin Ceram Soc, 2018, 37(3): 1077張西玲, 郭松林, 陳林, 等. 錳渣制備沸石分子篩的表征及鈣離子交換能力的研究. 硅酸鹽通報, 2018, 37(3):1077 [78] Miao X W, Bai Z T, Qiu G B, et al. Preparation of transparent Mn-doped CaF2 glass-ceramics from silicon-manganese slag: dependence of colour-controllable change on slag addition and crystallization behaviour. J Eur Ceram Soc, 2020, 40(8): 3249 doi: 10.1016/j.jeurceramsoc.2020.02.029 [79] Patil A V, Pande A M. Behaviour of silico manganese slag manufactured aggregate as material for road and rail track construction. Adv Mater Res, 2011, 255-260: 3258 doi: 10.4028/www.scientific.net/AMR.255-260.3258 [80] Huang D, Chen S H, Mon H H. The preliminary study on re-utilization of ferrous-nickel slag to replace conventional construction material for road construction (sub-grade layer improvement). Adv Mater Res, 2013, 723: 694 doi: 10.4028/www.scientific.net/AMR.723.694 [81] Zhang H B. Development of Ecological Water-Permeable Bricks Using Silicon-Manganese Slag [Dissertation]. Guiyang: Guizhou University, 2007張洪波. 利用硅錳渣研制生態滲水磚[學位論文]. 貴陽: 貴州大學, 2007 [82] Cheng H L, Zhang L, Dong R L, et al. Experimental research on permeable concrete with high carbon ferrochrome slag. Recyclable Resour Circular Economy, 2018, 11(1): 30 doi: 10.3969/j.issn.1674-0912.2018.01.010程海麗, 張亮, 董瑞龍, 等. 高碳鉻鐵合金渣透水混凝土試驗研究. 再生資源與循環經濟, 2018, 11(1):30 doi: 10.3969/j.issn.1674-0912.2018.01.010 [83] Li G C, Wang P. Study on preparation and performances of the water permeable brick from ferronickel slag. Multipurpose Utilization Mineral Resour, 2018(2): 97 doi: 10.3969/j.issn.1000-6532.2018.02.021李國昌, 王萍. 鎳鐵礦渣透水磚的制備及性能研究. 礦產綜合利用, 2018(2):97 doi: 10.3969/j.issn.1000-6532.2018.02.021 [84] Park J H, Kim S H, Delaune R D, et al. Enhancement of phosphorus removal with near-neutral pH utilizing steel and ferronickel slags for application of constructed wetlands. Ecol Eng, 2016, 95: 612 doi: 10.1016/j.ecoleng.2016.06.052 [85] Fu P F, Yang H F, Zhang G, et al. In-situ immobilization of Cd-contaminated soils using ferronickel slag as potential soil amendment. Bull Environ Contam Toxicol, 2019, 103(5): 756 doi: 10.1007/s00128-019-02719-6 -
點擊查看大圖
圖(4) / 表(4)
計量
- 文章訪問數: 4435
- HTML全文瀏覽量: 1785
- PDF下載量: 174
- 被引次數: 0